3004 Aluminum Bar

3004 Aluminum Bar

No content
Product Introduction
3004 aluminium alloy is an alloy in the wrought aluminium-manganese alloys family (3000 or 3xxx series). It is similar to the 3003 alloy, except for the addition of approximately 1% magnesium. It can be cold worked (but not, unlike some other types of aluminium alloys, heat treated) to produce tempers with a higher strength but a lower ductility. Like most other aluminium-manganese alloys, 3003 is a general-purpose alloy with moderate strength, good workability, and good corrosion resistance. It is commonly rolled and extruded, but typically not forged. As a wrought alloy, it is not used in casting.
3004 Aluminium Alloy Composition by Mass %
AlMgSiFeCuZnMnRemainder
95.6 to 98.2%0.8 to 1.3%0.3% max0.7% max0.25% max0.25% max1.0 to 1.5%0.15% max


Machinability

Aluminium / Aluminum  3004 alloy has good machinability in the hard temper. Oil lubricant is used for performing machining operations.

Forming

Aluminium / Aluminum  3004 alloy can be formed using conventional hot working or cold working methods.

Welding

The Aluminium / Aluminum  3004 alloy can be welded using TIG or MIG welding techniques.

Heat treatment

Aluminium / Aluminum  3004 alloy is a non-heat treatable alloy.

Forging

Aluminium / Aluminum  3004 alloy is forged at temperatures ranging from 372 to 510°C (700 to 950°F).

Hot Working

Aluminium / Aluminum  3004 alloy is hot worked at 260 to 483°C (500 to 900°F).

Cold Working

Aluminium / Aluminum  3004 alloy can be cold worked up to 75% reduction of area using conventional techniques. This process should be followed by annealing if it is cold worked beyond 75% reduction of area.

Annealing

Aluminium / Aluminum  3004 alloy is annealed at 344°C (650°F) followed by cooling in air.

Hardening

Aluminium / Aluminum  3004 alloy can be annealed by cold working.

Applications

Aluminium / Aluminum  3004 alloy is used in sheet metal work. It is also used in manufacturing storage tanks.


Application

Construction/Indutry/Building/Chemical/Auto

The alloy 3004 is commonly used in the making of beverage cans. It was developed to satisfy the need for thinner gauges in can-stock, and thereby to some extent replaced its predecessor 3003 alloy in the making of beverage cans. Can-stock can be made thinner due to the addition of 1% magnesium, which contributes in solid solution strengthening.




MESSAGE
NameRequiredNameSubmit exception
MobileRequiredMobileSubmit exception
EmailRequiredEmailSubmit exception
MessageRequired
CopyRight © Foshan Sewaly Steel Co., Ltd.
Message
NameRequiredNameSubmit exception
MobileRequiredMobileSubmit exception
EmailRequiredEmailSubmit exception
MessageRequired